Temperature and pH sensitive N-isopropyacrylamide-acrylic acid (NIPAAm-AA) and N-isopropylacrylamide-acrylic acid-butyl acrylate (NIPAAm-AA-BA) hydrogels were synthesized by simultaneous polymerization and crosslinking of NIPAAm AA, and BA monomers in aqueous solution using γ-rays from ^60Co source at room temperature. The measurements of equilibrium water content on the synthesized hydrogels were made at the temperature ranging from 5 to 40℃ and pH 2 and 7. The prepared hydrogels had temperature-sensitive (30~35℃) and pH-sensitive swelling behavior. The HIPAAm-AA and NIPAAm-AA-BA hydrogels were used in drug delivery systems for the controlled release of insulin Insulin has been shown to have binding sites for hydrophobic molecules. Thus, it is likely that insulin binds specifically to the butyl side. The gels including insulin were prepared by air drying or freeze drying after loading insulin in solution (14.1 IU/mL) at 5℃ and pH 7. Drug-gels were plated in simulated gastric fluid (SGF; pH 1.2) at 37℃ for 2 h and then at simulated intestinal fluid (SIF : pH 7.3). The insulin release of the drug-gels was examined by UY analysis.

N-isopropylacrylamide (NIPAAm)와 acrylic acid (AA)를 증류수에 일정한 몰비로 용해한 것과 여기에 butyl acrylate (BA)를 혼합한 용액을 상온에서 30, 50 kGy로 γ-선 조사하여 중합반응과 가교를 동시에 일으켜 pH 및 온도에 민감한 수화겔을 제조하였다. 제조된 수화겔은 pH 2, 7의 용액에서 5~40℃로 온도를 변화시켜 각각의 온도에서 최대 팽윤도를 측정하고 한편으로는 37℃로 고정한 후 PH 2~8까지 pH에 대한 최대 팽윤도를 측정하였다. 수화겔의 팽윤과 수축에 이온강도가 어떤 영향을 미치는지 알아보기 위해 0, 0.01, 0.03 N의 염화나트륨 용액에서 팽윤실험을 하였다. 경구용 인슐린 전달제재를 제조할 목적으로 수화겔이 최대 팽윤할 수 있는 최저의 온도와 pH 조건에서 인슐린을 탑재한 다음 자연건조(air dried)와 동결건조(freeze dried)를 하여 인슐린을 함유한 겔(drug-gels)을 제조하였으며, 인슐린 탑재 후 남은 인슐린 용액으로부터 탑재효율을 구하였다. Drug-gel은 in vitro에서 인공위액(simulated gastric fluid; SGF)과 인공장액(simulated intestinal fluid ; SIF)에서 약물 방출량을 측정하여 방출속도를 측정하였다.