In order to investigate the thermal stability of electro-conductive poly(3,4-ethylenedioxythiophene)-poly(styrene sulfonate) (PEDOT/PSS), we have prepared films by casting PEDOT/PSS aqueous solution without using a binding material and measured surface resistances of the films while annealing at 200 ℃. Electrical properties of films were improved by annealing, and the maximum conductivity (540 S · m-1) after annealing for 2 hrs was found to be approximately 3 times higher than that (180 S · m-1) of the original film. The conductivities, however, dramatically decreased with an increase in annealing time and dissipated after 24 hrs of annealing. On the other hand, PEDOT/PSS films hybridized with graphene oxide (GO) displayed a salient improvement in conductivity by annealing, which was measured to be around 600 S · m-1 even after 30 hrs of annealing at 200 ℃. We tentatively conclude that hybridization with GO enhances the thermal stability of PEDOT/PSS.

전도성 고분자인 PEDOT/PSS의 열적 안정성을 검토하기 위하여 바인딩 물질 없이 캐스팅하는 방법에 의해서 필름을제조하고, 200 ℃에서 annealing하면서 표면저항의 변화를 검토하였다. PEDOT/PSS 필름은 열처리에 의해서 전기적특성이 향상되었으며, 2 h 정도에서 최대 전도도값(540 S⋅m-1)을 나타내어 초기 값(180 S⋅m-1)에 비해서 3배 정도높아졌다. 그러나 시간이 지남에 따라 전기전도도가 떨어지고, 24 h이 지난 이후에는 거의 전기적 특성을 나타내지않았다. 한편, 산화 그래핀(GO)과 복합화한 PEDOT/PSS 필름에서는 열처리에 의한 전기적 특성의 향상이 더 뚜렷하였으며, 200 ℃에서 30 h 이상 보관하더라도 전기전도도가 600 S⋅m-1 정도를 유지하는 것으로 나타나, GO와의 복합화가 PEDOT/PSS의 열적 안정성을 현저하게 향상시키는 것을 확인할 수 있었다.