This study was to investigate the production of combustion toxic gases of pinus rigida specimens treated with pyrophosphoric acid (PP)/4ammonuium ion (4NH4 +), methylenepiperazinomethyl-bis-phosphonic acid (PIPEABP) and PIPEABP/4NH4 +. Each pinus rigida plates was painted in three times with 15 wt% in the aqueous solution followed by drying the species at room temperature. Emission of combustion toxic gases was examined by the cone calorimeter (ISO 5660-1). First-time to peak mass loss rate (1st-TMLR peak) treated with chemicals was delayed upto 66.7~250.0% compared to those of untreated specimens. For test pieces treated with the chemicals, the emission of peak carbon monoxide (CO peak) values of 0.0136~0.0178% and peak carbon dioxide (CO2 peak) value of 0.04432~0.3648% were obtained, which were higher than those for the virgin plate. In particular, oxygen emission is much higher than the level of 15% which can be fatal to humans. Therefore, the resulting risk could be eliminated. However it is supposed that the combustion-toxicities were partially increased compared to those of virgin plate.

이 연구에서는 피로인산/4암모늄이온, 메틸렌피페라지노메틸-비스-포스폰산, 메틸렌피페라지노메틸-비스-포스폰산/4암모늄이온의 화학 첨가제로 처리된 리기다 소나무의 연소독성가스의 생성을 고찰하였다. 15 wt%의 화학 첨가제 수용액으로 각각 리기다 소나무에 3회 붓칠하여 실온에서 건조시킨 후, 콘칼로리미터(ISO 5660-1)를 이용하여 연소독성가스의 생성을 시험하였다. 그 결과, 화학 첨가제로 처리한 시험편의 1차-최대질량감소율도달시간(1st-TMLR peak)은 무처리 시험편에 비교하여 (66.7~250.0)%의 지체된 시간을 나타내었다. 반면에 첨가제로 처리한 시험편에 대한 최대 일산화탄소 생성(CO peak), (0.0136~0.0178)% 및 최대이산화탄소 생성(CO2 peak), (0.04432~0.3648)%은 공시험편보다 높게 나타났다. 특별히 O2의 생성농도는 사람에게 치명적일 수 있는 수준인 15%보다는 훨씬 높으므로 그로 인한 위험성은 배제할 수 있었다. 그러나 화학 첨가제로 처리한 시험편은 처리하지 않은 시험편과 비교하여 연소-유독성을 부분적으로 증가시켰다.