It is essential to employ a binder to prepare transparent films from conductive polymer such as poly(3,4-ethylenedioxythiophene)- poly(styrene sulfonate) (PEDOT/PSS). In this paper, poly(vinyl alcohol) (PVA), poly(vinyl pyrrolidone) (PVP), and PSS were selected as a binder, and their effects were investigated. The formation of the film was found to be primarily dependent on the surface tension of coating solution including PEDOT/PSS and a binder. When PSS was used as a binder, the film was not formed. In case of using PVP, it was easily peeled off from the substrate. However, when using the PVA or the mixtures of PVA and PSS or PVA and PVP as a binder, films with good transparency and uniform surface resistances were produced. Based on adhesion and long-term stability tests, we concluded that the mixture of PVA and PSS is the best binder for preparing antistatic films of PEDOT/PSS.

전도성 고분자인 poly(3,4-ethylenedioxythiophene)-poly(styrene sulfonate) (PEDOT/PSS)의 투명한 필름을 제조하기 위해 서는 바인더의 사용이 반드시 필요하다. 본 연구에서는 poly(vinyl alcohol) (PVA), poly(vinyl pyrrolidone) (PVP) 및 PSS를 바인더로서 검토하여 그 특성을 비교하였다. PEDOT/PSS 필름의 형성 여부는 기본적으로 바인더를 포함하는 코팅액의 표면장력 값에 의존하였다. PSS 또는 PVP를 바인더로 사용하였을 때는 필름이 형성되지 않거나 필름이 기재로 부터 쉽게 박리되는 현상이 나타났다. 그러나 PVA를 단독으로 사용하거나 또는 PSS 및 PVP를 PVA와 혼합하여 사용 하면 투명하며 균일한 표면저항 값을 나타내는 대전방지 필름을 얻을 수 있었다. 필름의 접착력 및 장기 보관 안정성 등을 종합적으로 판단하면, PEDOT/PSS의 대전방지용 필름을 제조하기 위한 바인더로서는 PVA와 PSS의 혼합물이 최적인 것으로 나타났다.