In this study, nanosized TPA-silicalite-1 was synthesized with a suitable molar composition of TPAOH: SiO2: H2O for thedevelopment of zeolite ceramic membranes to utilize as gas separation. As silica sources, TEOS, LUDOX AS-40 andCAB-O-SIL were used with the starting material of TPAOH. NaH2PO4, and a variety of acids and bases were used as promotersafter TPAOH, SiO2, H2O gel synthesis. To decrease synthesis time, a two step temperature change method was appliedto the synthesis of TPA-silicalite-1 at a low temperature. TPA-silicalite-1 synthesized was analyzed with XRD, SEM, BETand TGA. As a result, TPA-silicalite-1 powders with a particle size of 100 nm and a specific surface area of 416 m2/g wereobtained as optimum synthesis conditions when the two stage temperature change method was used with NaH2PO4 as promoter.

본 연구에서는 기체 분리를 위한 제올라이트 세라믹 멤브레인 제조에 적합한 입자크기와 형상을 갖춘 나노크기의 제올라이트를 TPAOH : SiO2 : H2O의 적합한 조성으로 합성하였으며 그 특성을 분석하였다. 실리카 원으로는 TEOS,LUDOX AS-40, CAB-O-SIL을 사용하고, TPAOH와 함께 출발물질로 하여 특정 조성의 TPAOH, SiO2, H2O gel을 합성하고, NaH2PO4 및 다양한 산 염기를 결정화 촉진제로 사용하였다. 합성시간을 단축할 수 있는 방법의 일환으로 저온에서2단계 온도 변화법을 적용한 수열합성법으로 TPA-Silicalite-1을 합성하였으며 XRD, SEM, BET, TGA 등을 사용하여분석하였다. 그 결과, 2단계 온도 변화법을 사용하고, 결정화 촉진제로서 NaH2PO4를 사용하였을 때가 최적의 합성 조건으로 입자크기100 nm, 비표면적 416 m2/g의 TPA-Silicalite-1 분말을 제조할 수 있었다.