Microstructure and thermal stability of mechanically ball milled $FeS_2$ 수식 이미지 were investigated. The average particle size and distribution of $FeS_2$ 수식 이미지 powder were changed in two steps with the increased ball milling time. The average particle size drastically decreased from $98.4{\mu}m$ 수식 이미지 to 1.01 and $0.89{\mu}m$ 수식 이미지 after ball milling of 10 h and 30 h, respectively. However, the distribution was broad and a shoulder appeared at $2{\mu}m$ 수식 이미지 because the pulverization was still in process at 10 h ball milling. After 60 h ball milling, the distribution became narrower. After ball milling of 120 h, the average particle size increased because of $FeS_2$ 수식 이미지 particle agglomeration. Therefore, the particle size distribution became broaden again. Finally, after ball milling of 170 h, $FeS_2$ 수식 이미지 with the narrowest size distribution can be obtained. Thermal stability of $FeS_2$ 수식 이미지 was unstable as the $FeS_2$ 수식 이미지 particle was pulverized. Therefore, the activation energy of the fine size particles is 27% lower than that of the as-received $FeS_2$ 수식 이미지.

FeS2 미세 입자가 열전지의 특성에 미치는 영향을 알아보고자, 볼밀법을 이용하여 미세화 입자를 제조하고 그 미세 구조 및 열안정성을 평가하였다. FeS2의 평균 입자크기와 입자분포는 볼밀 시간에 따라 변하였다. 평균 입자크기는 10 h 볼밀 처리 후, 98.4 μm에서 1.01 μm로 급격하게 감소하였다. 볼밀 시간이 증가할수록, 입자의 응집이 증가하고 입자 크기의 분포가 넓어지기 때문에 평균 입자크기는 증가하였다. 결국, 170 h의 볼밀을 시행한 후에 가장 좁은 크기의 단일 입자 분포를 가지는 FeS2 미세 입자를 얻을 수 있었다. 한편, 입자가 분쇄됨에 따라 FeS2의 열 안정성은 불안정해 졌으며, 미세 입자 사이즈의 활성화 에너지는 이전의 FeS2보다 27% 낮아졌다.