In this work, we have prepared tungsten doped vanadium oxide (W-VO2) particles with a low phase transition temperature. W-VO2 particles were synthesized via thermolysis method using vanadyl (IV) sulfate and ammonium bicarbonate as precursors. The structure and thermochromic property of synthesized W-VO2 particles were investigated by FE-SEM, EDS, XRD, XPS, and DSC analysis. The prepared W-VO2 showed a nearly platy morphology, which indicates that the tungsten was successfully doped in the crystal lattices of VO2. W-VO2 nanoparticles with the size of 60 nm exhibited a monoclinic crystal structure and its chemical composition and surface state were also likely to be close to that of VO2. In addition, the phase transition temperature of W-VO2 was 38.5 ℃, which was approximately 29.2 ℃ lower than that of pure VO2 (67.7 ℃), indicating that the prepared sample had a good reversible thermochromic stability.

본 연구에서는 낮은 열전이 온도를 가지는 텅스텐이 도핑된 이산화바나듐(W-VO2)을 제조하였다. 텅스텐이 도핑된 이산화바나듐은 바나딜설페이트(VOSO4)와 중탄산암모늄((NH4) HCO3)을 전구체로 열분해 과정을 통해 제조하였다. 이에 대한 입자의 구조 및 열전이 특성을 FE-SEM, EDS, XRD, XPS, DSC 분석을 통해 조사하였다. 그 결과 텅스텐이 도핑된 이산화바나듐 입자의 형상은 판상형태로 텅스텐이 이산화바나듐 결정에 잘 도핑 되어 있음을 확인 하였다. 텅스텐이 도핑된 이산화바나듐의 결정 구조는 단사정으로 60 nm의 크기를 가지고 있었으며, 화학적인 조성 및 표면 상태는 이산화바나듐과 유사하였다. 또한, 텅스텐이 도핑된 이산화바나듐의 상전이 온도는 38.5 ℃로 순수한 이산화바 나듐의 상전이 온도인 67.7 ℃에 비해 29.2 ℃ 낮게 나타났으며, 가역 상전이 안정성이 우수하였다.