The ε type copper phthalocyanine (ε-CuPc), called as a pigment blue 15 : 6, is a significant material to produce a blue pixel in LCD (Liquid Crystal Display) panel. In this study, ε-CuPc sample was synthesized at various reaction conditions by applying the seed method using ε-CuPc nanoparticles as a seed. Adequate synthetic conditions of the samples were selected by analyzing and comparing crystalline structure, crystalline purity, microstructure, and synthetic yield of the samples with α and β crystalline CuPc samples. The chemical and crystalline structure of the samples were tested using FT-IR spectrometer and X-ray diffractometry, respectively. The shape of the particle was examined using field emission scanning electiron microscope while the thermal property was tested utilizing thermogravimetric analysis.

블루 안료 15 : 6이라 불리는 ε결정상의 동프탈로시아닌(ε-CuPc)는 LCD 패널에서 청색화소를 제공하는 중요한 소재로써, 본 연구에서는 ε-CuPc 시료를 ε-CuPc 나노 입자를 seed로 이용하는 방법으로 여러 조건에서 합성하여 적합한 용매 및 온도조건 등을 규명하였고, 이를 미리 합성한 α 및 β 결정상의 CuPc 시료들과 비교함으로써 ε-CuPc 시료의 결정상, 결정 순도, 합성 수율 및 미세구조를 상호 비교·분석하였다. 시료들의 화학 구조 및 결정 구조는 푸레어 변환적외선(FT-IR) 분광기 및 X선 회절 분석기(XRD)를 이용하여 각각 비교 분석하였다. 또한, 입자의 형상 및 크기는 주사 전자현미경(FE-SEM)으로 비교 분석하였고, 열적 특성은 열중량분석기(TGA)를 이용하여 비교 분석하였다.