Polystyrene latex spheres (PLS) were prepared as artificial dusts by the emulsion polymerization with potassium persulfate (KPS) and sodium dodecyl sulfonate (SDS) as an initiator and a stabilizer, respectively. The reaction temperature and the concentration of the initiator and stabilizer were chosen as variables to control the PLS particle size. As temperature increased, the particle size decreased considerably. Furthermore, the PLS particle size and their size distributions can be controlled minutely by adjusting the concentrations of KPS and SDS. It is confirmed that the PLS prepared in this work is monodispersed with the coefficient of variance less than 7% and are in the range of 0.1∼0.5 μm, which are good for using as artificial dusts.

potassium persulfate (KPS)와 sodium dodecyl sulfonate (SDS)를 각각 개시제와 안정제로 사용한 유화중합에 의하여 인공 먼지로 사용할 수 있는 polystyrene latex spheres (PLS)를 제조하였다. PLS입자의 크기를 조절하기 위한 변수로 반응온도와 개시제 및 안정제의 농도가 선택되었다. 반응온도의 증가에 따라 입자의 크기는 작아졌으며, KPS와 SDS의 농도를 변화시켜 PLS 입자의 크기 및 분포를 매우 미세하게 조절할 수 있었다. 본 연구에서 제조된 PLS입자는 변동계수(CV) 값이 7% 이하인 단분산이며, 0.1∼0.5 μm 범위에 있어 인조 먼지로 사용하기에 적합한 것으로 밝혀졌다.