The cathodic active material of Li/SO2Cl2 battery is SO2Cl2, which is the solvent of an electrolyte. It is referred to as a catholyte, a compound word of cathode and electrolyte. As the battery discharges, the catholyte burns out. And thus, the characteristics of the SO2Cl2 in the battery determine the capacity. In addition, the transition minimum voltage (TMV) and the voltage delay deviation of Li/SO2Cl2 battery are due to the passivation film formed by the reaction between an electrolyte and Li. Impurities in the electrolyte, such as moisture or heavy metal ions, will accelerate the growth of the passivation film. Therefore, a technology must be established to purify an electrolyte and to ensure the effectiveness of the purification method. In this research, LiAlCl4/SO2Cl2 was manufactured using AlCl3 and LiCl. Its concentration, the amount of moisture, and the metal amount were evaluated using an ionic conductivity meter, a colorimeter, and FT-IR.

Li/SO2Cl2 전지의 양극활물질은 SO2Cl2인데 이 물질은 전해액의 용매이기도 하다. 이를 일컬어 catholyte (cathode와 electrolyte의 합성어)라 칭하는데 전지의 방전이 진행됨에 따라 소진된다. 따라서 전지 제작 시 투입되는 SO2Cl2의 특성은 전지의 용량을 결정하는 중요 변수이다. 또한, Li/SO2Cl2 전지의 transition minimum voltage (TMV)와 전압지연 편차는 전해액과 리튬의 반응에 의하여 형성된 부동화 막과 관련되는데 이 부동화 막은 전해액 내 불순물(수분 또는 중금속 이온)이 있을 경우 이의 성장이 촉진된다. 따라서 전해액을 정제시키는 기술과 이를 평가하는 방법의 정립은 반드시 필요하다. 본 연구에서는 LiAlCl4/SO2Cl2전해액을 AlCl3와 LiCl을 이용하여 제조하였고 제조된 전해액을 이온전 도도계와 색도계 및 FT-IR을 이용하여 농도와 수분, 금속함량 등을 평가하였다.