In order to improve the energy conversion efficiency of dye-sensitized solar cell (DSSC), the photoelectrode was manufactured by using TiO2 and WO3 on combination effects of two conduction bands. The smash procedure of TiO2 and WO3 was carried out by using a paint shaker to enlarge the contact area of semiconductor with dye and electrolyte. The energy conversion efficiency of prepared DSSC was improved about two times from current-voltage curve based on effects of WO3 and smash. The mechanism was suggested that the conduction band of WO3 worked for prohibiting the trapping effects of electrons in conduction band of TiO2. This result is attributed to the prevention of electron recombination between electron in conduction band of TiO2 with dye and electrolyte. Impedance results indicate the improved electron transport at interface of TiO2/dye/electrolyte.

염료 감응형 태양전지의 에너지 전환 효율을 향상시키고자 TiO2에 WO3을 첨가하여 광전극을 제조하고 그 전기화학적 특성 평가를 하였다. 또한 WO3가 첨가된 TiO2를 회쇄함으로써 회쇄 효과가 전지효율에 미치는 영향을 고찰하였다. I-V 곡선을 통하여 측정된 염료 감응형 태양전지의 효율은 WO3 첨가 및 회쇄 효과에 의하여 2.8에서 6.0%로 크게 증가하였다. 이와 같은 결과는 TiO2의 전도대에서 전달되는 전자가 염료 및 전해질과 재결합되기 전에 TiO2의 전도대 보다 낮은 WO3의 전도대를 통해 전달되기 때문에 전체 전류의 양이 증가되어 효율이 증가한 것으로 여겨진다. 또한, 임피던스 결과로부터 TiO2/염료/전해질 계면의 저항 값이 감소하는 것을 확인하였다.