In this study, binderless zeolite BaX granule, an effective adsorbent for the separation of p-xylene was made. This adsorbent which has a sufficient strength, high specific surface area and selectivity to p-xylene was prepared by various steps, such as granulation process, calcination, binderless treatment, ion-exchange, and activation. In the granulation, the concentration of colloidal silica solution was controlled in order to confirm the effect of SiO2 contents after binderless treatment. As a result, we confirmed that the compressive strength of granule after binderless treatment was increasing with increasing proportion of SiO2 in the granule. And then Na-ion in granule was exchanged with Ba-ion by successive batch ion-exchange process. And then prepared adsorbents were tested for p-xylene separation by batch adsorption at 90 ℃. As a results of batch adsortion test, we confirmed that prepared adsorbents have a high selectivity to p-xylene. Also, it could be conformed that the prepared binderless zeolite BaX has a sufficient compressive strength (0.450 kgf), high specific surface area (647.57 ㎡/g), high crystallinity (98.5% compared with zeolite NaX powder), and selectivity to p-xylene.

파라자일렌 분리용 흡착제로서 효과적인 결합제가 없는 제올라이트 BaX 성형체를 제조하는 방법에 대하여 검토하였다. 제올라이트 NaX 타입의 결정분말을 무기결합제인 colloidal silica sol (C.S.) 용액과 기공형성제인 microcrystalline cellulose 분말을 이용하여 구형화 한 후 소성, binderless 처리, 바륨 이온교환, 활성화 등의 단계를 거치면서 넓은 비표면적과 우수한 강도 및 파라자일렌에 대한 선택도를 갖는 파라자일렌 분리용 흡착제를 제조하였다. 각 시료의 무기결합제(SiO2)함량을 14.0 wt%, 18.0 wt%, 22.3 wt%로 조절하여, 무기결합제의 함량 증가에 따른 시료 강도의 변화에 대해 검토하였다. 구형화 시료의 무기결합제 함량이 증가 될수록 binderless 처리 후의 강도가 증가함을 확인할 수 있었다. 이렇게 제조된 시료에 무게비 1 : 1 : 1로 혼합된 혼합자일렌 용액으로 90 ℃에서 회분식 흡착실험을 수행해본 결과, 본 연구에서 제조된 binderless zeolite BaX는 파라자일렌에 선택적인 흡착능을 보임을 확인하였다. 이렇게 제조된 흡착제는 충분한 강도(0.450 kgf)와 결정화도(98.53%), BET 비표면적(647.57 ㎡/g)을 가지면서, 파라자일렌을 선택적으로 흡착함을 확인할 수 있었다.