The generation of high-purity hydrogen from hydrocarbon fuels is essential for efficient operation of fuel cell. In general, most feasible strategies to generate hydrogen from hydrocarbon fuels consist of a reforming step to generate a mixture of H2, CO, CO2 and H2O (steam) followed by water gas shift (WGS) and CO clean-up steps. The WGS reaction that shifts CO to CO2 and simultaneously produces another mole of H2 was carried out in a two-stage catalytic conversion process involving a high temperature shift (HTS) and a low temperature shift (LTS). In a typical operation, gas emerges from the reformer is taken through a high temperature shift catalyst to reduce the CO concentration to about 3∼5%. The HTS reactor was designed and tested in this study to produce hydrogen-rich gas with CO to a range of 2∼4%. The iron based catalysts (G-3C) was used for the HTS to convert the most of CO in the effluent from the partial oxidation (POX) to H2 and CO2 at a relatively high rate. Parametric screening studies were carried out for variations of the following variables: reaction temperature, steam flow rate, components ratio (H2/CO), and reforming gas flow rate.

탄화수소 계열의 연료로부터 고순도의 수소를 생산하는 것은 연료전지의 효율적인 운전과 밀접하다. 일반적으로 대부분의 탄화수소 연료에서 수소를 생산하는 과정은 수소, 일산화탄소, 이산화탄소와 수증기 혼합물이 생성되는 개질 과정 및 일산화탄소를 저감하는 전이반응과 선택적 산화반응 과정으로 구성되어 있다. 전이반응은 일산화탄소를 이산화탄소로 전환하는 동시에 수소가 생성되는 고온 전이와 저온전이로 구성된 두 단계의 촉매전환 공정이다. 일반적으로 개질기에서 생성된 개질 가스는 고온전이 반응기를 거쳐 일산화탄소 농도를 3∼5%까지 저감한다. 본 연구에서는 고온전이 반응기를 설계 및 제작하여 일산화탄소 농도를 2∼4%까지 저감하였다. 고온전이 반응에서 철이 첨가한 촉매(G-3C)를 사용하여 부분산화 개질에서 생성된 일산화탄소를 이산화탄소로 전환하였다. 그리고 고온전이 영향인자인 수증기 주입량, 개질 가스 조성, 반응온도, 개질 가스 주입량변화에 대한 연구를 진행하였다.