The removal characteristics of ionic species, such as Ca2+, Mg2+, Sr2+, SO42-, NO3-, and Cl- by adsorption on the alumina were investigated. Alumina precusor powders were prepared from Al(NO3)39H2O and NH4OH. Alumina materials prepared from the heat treatment in a furnace at 450∼750 ℃ for 5 h were analysed using FT-IR and the Brunauer- Emmett-Teller (BET) method. The specific surface area of the product particles decreased significantly with treatment temperature. The adsorption capacities of SO42- and NO3- on alumina were 23 mg/g and 12.4 mg/g, respectively. But, removal efficiencies of Cl- were less than 4 mg/g. In general, the removal efficiencies of the anion species were decreased with increasing treatment temperature. The best anion removal efficiency was obtained when the alumina was treated under 450 ℃. Removal efficiencies of Ca2+, Mg2+, and Sr2+ were increased with increasing treatment temperature.

본 연구는 알루미나를 이용하여 수용액 중에 존재하는 Ca2+, Mg2+, Sr2+, SO42-, NO3-, Cl- 이온의 제거 특성을 분석하기 위하여 실시하였다. 알루미나는 Al(NO3)39H2O와 NH4OH를 사용하여 합성한 수화물을 450∼750 ℃로 5 h 동안 열처리하고 FT-IR과 Brunauer-Emmett-Teller (BET)법으로 물성을 분석하였다. 실험결과에 의하면 알루미나의 비표면적은 열처리 온도가 증가하면 감소하는 특성을 나타내었다. 알루미나에 의한 흡착능은 SO42-와 NO3-가 각각 23 mg/g와 12.4 mg/g의 값을 보였다. 반면에 Cl-는 4 mg/g으로 비교적 낮은 값을 보였다. 일반적으로 음이온 제거 효율은 알루미나의 제조를 위한 열처리 온도가 증가할수록 감소하였으며, 450 ℃로 처리한 알루미나의 경우에 가장 좋은 처리 효율을 나타내었다. 양이온인 Ca2+, Mg2+, Sr2+의 제거 효율은 알루미나의 열처리 온도에 비례하여 증가하는 경향을 보였다.