Semi-solvent type cleaning agents were prepared by mixing naphthenes, natural terpene oil, surfactant and water, and measured their physical properties. And also, cleaning efficiency for flux and grease was measured by gravimetric method. By measuring the physical properties, pH for cleaning agents were 6.0∼6.7, surface tension, 27.4∼28.4 dyne/cm, and wetting index, 8.65∼12.46 (with water), 11.99∼17.43 (without water). The cleaning agent composed of naphthene, 30 wt%, natural terpene oil, 45 wt%, surfactant, 13 wt%, co-surfactant, 12 wt%, and water, 0 wt% had the largest wetting index, and shown the most effective cleaning properties for flux (98.66%) and grease (93.44%). The conductivity with 0.5∼0.9 μs/cm to the cleaning agent containing small amount of water was found to form W/O type microemulsion.

나프텐계 탄화수소, terpene계 천연 용제, 계면활성제 및 물을 이용하여 친환경적 준용매계 세정제를 제조하고 이들의
물리적 특성과 flux 및 grease 오염물에 대한 세정효율을 측정하였다. 준용매계 세정제의 물성은 pH가 6.0∼6.7의 약산
성으로 중성에 가까운 값을 나타내었으며 표면장력은 27.4∼28.4 dyne/cm의 값을 나타내었다. 또한 wetting index는 물
이 소량 들어간 경우 8.65∼12.46, 물이 들어가지 않은 경우 11.99∼17.43의 값을 가졌으며 나프텐계 탄화수소 30 wt%,
terpene계 천연 용제 45 wt%, 계면활성제 13 wt%, 보조계면활성제 12 wt%, 물 0 wt%의 조성으로 제조한 세정제가
17.43으로 가장 큰 값을 가졌으며 세정 효율 역시 flux에 대하여 98.64%, grease에 대하여 93.44%로 우수하였다. 전기
전도도는 소량의 물을 첨가한 경우 0.5∼0.9 µs/cm의 값을 나타내어 물이 용제 중에 균일하게 분산되어 있는 W/O형의 준용매계 세정제임을 확인하였다.