A study on the polymerization of polyethylenedioxythiophene (PEDOT) and the carbonization process of a separator was carred out in order to apply conductive polymer PEDOT to the winding typed aluminum condenser as a solid electrolyte and a negative electrode. PEDOT was polymerized with ethylenedioxythiophene (EDOT) as a monomer and ferric-p-toluenesulfonate as an oxidizing agent. The separator of condenser element was carbonized to control its fibrous tissue for the purpose of making it easy to impregnate the PEDOT solution into the microporous etched pit of aluminum foil by preventing separator from concentrating the PEDOT solution on itself. The characteristics of condenser such as capacitance, dissipation factor, equivalent series resistance, and thermal resistance depended on a carbonization temperature and a carbonization time. It was found that a thickness and a density of the used separator were major parameters of carbonization process and the characteristics of condenser were affected by these parameters.

전도성 고분자인 polyethylenedioxythiophene (PEDOT)을 권취형 알루미늄 콘덴서의 고체 전해질 및 음극으로 적용하기 위 하여 PEDOT 중합공정 및 절연지 탄화공정 연구를 수행하였다. 단량체로 ethylenedioxythiophene (EDOT), 산화제로 ferric-p-toluenesulfonate를 사용하였다. 권취된 미세 다공성 알루미늄 에칭박 피트 내부에 균일한 PEDOT 전해질 층을 생 성하기 위하여 콘덴서 소자를 열처리하여 탄화함으로써 절연지의 섬유조직을 조절하고 이를 통해 중합액의 절연지 집중현 상을 억제하여 에칭 피트 내부로의 중합액 함침이 용이하도록 하였다. 탄화온도, 탄화시간에 따라 콘덴서의 용량, 손실, 등가직렬저항, 내열특성이 좌우되었다. 절연지의 두께, 밀도는 탄화공정의 중요한 변수이며 이들 변수에 따라 콘덴서의 특성이 영향을 받는 것을 확인하였다.