The leaching behaviors of zinc and manganese oxides of spent alkaline manganeses battery in sulfuric acid solution by using H2O2 as a reducing agent were investigated according to the concentration of H2SO4, temperature, reaction time, and the amount of H2O2. The experimental results of zinc and manganeses dissolution rates obtained without a reducing agent at 100 g/L solid/liquid ratio, 3.0 M H2SO4, 60 ℃ and 200 r.p.m. were 97.7% and 43.5%, respectively. On the other hand, zinc and manganeses dissolution rates obtained by adding 30 mL reducing agent at 60 ℃ were 99.6% and 97.1%, respectively. The addition of the reducing agent increased the leaching of manganese by two-fold compared to the absence of a reducing agent. In case of adding over 30 mL H2O2, however, the leaching rates of zinc and manganeses were independent of reducing agent amounts.

망간산화물과 아연이 혼재되어 있는 폐알카리 망간전지로부터 황산용액에서 환원제로 과산화수소를 이용하여, 침출제 농도, 온도, 반응시간, 과산화수소의 양 등을 변화시키면서 망간과 아연의 침출거동을 조사하였다. 그 결과 고액농도 100 g/L, 황산 농도 3.0 M, 반응온도 60 ℃, 교반속도 200 r.p.m. 그리고 과산화수소를 첨가하지 않은 조건에서 아연과 망간의 침출율은 각각 97.7 %와 43.5 %를 나타내었으나, 반응온도 60 ℃에서 과산화수소 30 mL를 첨가하였을 때는 아연과 망간의 침출율은 각각 99.6 %와 97.1%를 나타내어 환원제를 첨가하지 않은 조건보다 망간의 침출율이 약 2배 정도 증가하였다. 그러나 과산 화수소 양이 30 mL 이상에서는 첨가되는 과산화수소의 양이 증가하여도 아연과 망간의 침출율의 변화는 거의 없었다.