In this study, PEO blend fibers mixed with polyaniline (PANI)/10-camphor sulfonic acid (CSA) and PANI/dodecylbenzene sulfonic acid (DBSA) were electro spun to investigate the influence of PANI content. CSA and DBSA were used as a functionalized doping acid having a bulky volume. PANI/PEO blend solution was prepared by dissolving PEO and PANI doped with CSA or DBSA. The thermal properties were measured by thermogravimetric analyzer (TGA). As a result, with increasing of the PANI content in PANI/CSA and PANI/DBSA, although initial decomposition temperature(IDT) was decreased, thermal stability was increased due to the increase of A*ㆍK* and integral procedural decomposition temperature (IPDT). The electrical conductivities measured by the 4-probe method. The electric conductivity was increased with increasing of PANI content in PANI/CSA and PANI/DBSA. However, electrical conductivity did not change significantly beyond 30% content of PANI. From CV results, PANI/CSA showed the better defined peak shpae and higher peak current density compared to PANI/DBSA. This was probably related to the slightly higher electrical conductivity or better morphology for easy charge transfer in the case of PANI/CSA.

본 연구에서는 폴리아닐린(PANI)을 제조하여 큰 분자량의 유기산인 10-camphor sulfonic acid (CSA) 또는 dodecyl-benzene sulfonic acid (DBSA)로 도핑시키고, polyethylene oxide (PEO)와 함께 블렌딩하여 전기방사 용액을 제조하였다. 제조된 용액을 전기방사하여 섬유형태로 만든 후, TGA와 전기화학 장치(cyclic voltammetry; CV)로 열적, 전기적 성질을 CSA 또는 DBSA로 도핑된 PANI의 함량에 따라 비교 분석하였다. 본 실험 결과, PANI-CSA와 PANI DBSA의 함량이 증가함에 따라 열분해 개시온도는 감소하지만 열안정성 지수와 적분 열분해 진행온도가 증가하는 것으로 보아 열안정성은 증가하는 것으로 판단된다. 또한, 전기전도도는 PANI-CSA와 PANI-DBSA의 함량이 증가함에 따라 증가하였으나 30% 이상이 되면 전도도가 일정해지는 것으로 나타났다. 순환전류젼압 곡선 결과, PANI/CSA는 PANI-DBSA 보다 피크가 좀 더 명확해지며, 전류밀도가 크게 나타났다. 이는 PANI-CSA가 약간 더 높은 전기전도도와 전하가 이동하기 쉬운 모폴로지를 가지고있기 때문인 것으로 판단된다.