Porous hydrated lime and limestone filters were prepared by foaming and gelcasting method, and their physical properties were evaluated. Through these analyses, it has been found that with the increased porosity and pore size of the filters, majority of pores in the filters were inter-connected by windows. Also, SO2 removal efficiency for the filters was investigated. As the porosity and the reaction temperature increased, SO2 removal efficiency also increased. Especially, unlike the variation of entrance concentration, the entrance flow rate had great influence on the removal efficiency. In case of the filters with an equal porosity, the hydrated lime filter had superior removal efficiency compared to the limestone filter. From these results, it was shown that the high conversion ratio to CaO from the hydrated lime filter was a result of facilitated formation of CaSO4 by SO2.

본 연구에서는 발포법 및 겔-캐스팅법을 이용하여 소석회와 석회석을 원료로 다공성 필터의 제조를 제조하였다. 제조된 필터의 물성과 SO2 제거성능을 평가한 결과 다공성 석회질 필터의 기공률 및 기공크기가 클수록 수많은 윈도우에 의해서 대부분의 기공이 열린 기공으로 형성됨을 알 수 있었다. SO2 제거에 대한 다공성 석회질 필터의 영향은 다음과 같이 관찰되었다. 반응온도가 증가할수록 SO2 제거효율은 증가하였다. SO2 유입농도에 따른 제거 효율의 차이가 많이 나지 않았지만 유량 차이에 의한 효율 변화는 상대적으로 크게 나타났다. 필터의 경우 기공률이 클수록 SO2 제거효율은 우수하였으며, 기공률이 동일한 경우에서는 소석회 필터는 석회석 필터보다 SO2 제거효율이 우수하였다. 이것은 소석회의 CaO 전환율이 석회석에 비해 우수하여 SO2에 의해 상대적으로 쉽게 CaSO4로 형성되었기 때문으로 판단된다.