To evaluate the posterior and anterior restoration of polymeric dental restorative composite (PDRC), PDRC was prepared using a silica filler treated by heat at various temperatures. Compressive strength (CS) and diametral tensile strength (DTS) values were investigated to study the effect of a heat-treated silica on the mechanical properties of PDRC using the recommended dental specifications. Both the particle size and specific volume of silica were decreased upon increasing the heat treatment temperature. CS and DTS values of PDRC containing a heat-treated silica showed 1.2 and 1.3 times, respectively, higher than that of the PDRC containing a neat silica. Also, it was found that the lower heat treatment temperature, the better mechanical properties of PDRC were observed because there was less agglomeration between silica particles. Specially, PDRC using a silica treated at 600 ℃ showed superior mechanical strength.

치아수복용 고분자 복합체(polymeric dental restorative composite, PDRC)의 전치부 및 구치부에의 응용 가능성을 높이고자 PDRC를 구성하는 실리카 충진재를 다양한 온도에서 열처리시켜 제조하고 제조된 PDRC의 기계적 물성을 압축강도와 간접인장강도 등을 분석하여 고찰하였다. 실험 결과, 열처리 온도가 상승함에 따라 실리카 입자 크기와 비표면적은 감소하였음을 확인하였으며 열처리시킨 실리카 충진재를 PDRC 제조에 사용한 결과, 열처리시키지 않은 실리카를 사용한 경우보다도 압축강도가 20%, 간접인장강도는 약 30% 정도 향상됨을 확인하였다. 또한 열처리 온도가 높아질 경우 실리카의 응집화로 인해 제조된 PDRC의 기계적 물성이 전반적으로 떨어지는 경향을 나타내었으며 600 ℃ 정도에서 열처리된 실리카를 사용하여 제조한 PDRC의 경우가 강도 면에서 보다 더 우수하였다.