The microbial cellulose is in a form of three dimensional net structures that consists of 20~50 nm fibrils. It possesses high crystallinity and orientation. It is difficult to synthesize large amount of fibrous carbon nanomaterials by the carbonization process using raw materials such as polyacrylonitrile (PAN), regenerated cellulose (Rayon) and pitch. However, it seems possible thru the application of microbial cellulose as raw material. The application of such cellulose can be further extended to the synthesis of highly oriented graphite fiber. Out of three different cellulose-producing strains, G. xylinus ATCC11142 was chosen as it has the highest productivity (0.066 g dried cellulose/15 mL medium). Tar is often produced during the carbonization of cellulose that limits the formation fibrous structure of the carbonized sample. In order to solve such a problem, pre-studied purification methods of carbon nanotube such as liquid phase oxidation, gas phase oxidation and filtration associatedwith ultrasonication were applied at the carbonized cellulose. In that case. only by filtration associated with ultrasonication, improved the formation of fiber structure of the carbonized cellulose.

미생물에 의해 생산된 셀룰로오스는 고등식물을 이루고 있는 셀룰로오스보다 순수한 형태로 존재하고 굵기가 20~50 nm인 fibril이 높은 배향성과 결정성으로 3차원적 망상구조를 이루고 있다. 이러한 미생물 셀룰로오스를 이용한 탄화과정의 적용은 기존의 PAN, Pitch, 재생 셀룰로오스(Rayon)를 사용한 탄소 섬유의 제조에서 얻지 못하는 섬유 구조 탄소 물질의 대량 생산을 가능하게 하고 탄화과정에 의해 생산된 섬유 구조의 탄화 셀룰로오스는 높은 결정성과 배향성을 갖는 나노 영역의 흑연 결정상의 섬유 제조를 가능하게 할 것이다. 탄화에 사용되는 셀룰로오스의 생산성에 대하여 세 가지 균주들에서 생산된 셀룰로오스의 양을 비교하여 G. xylinus ATCC 11142가 15mL 배지당 건조 질량 0.066 g의 셀룰로오스를 생산하는 것을 확인하였고 셀룰로오스의 탄화과정에서 셀룰로오스의 열분해에 의해 생산된 타르(tar)에 의해 탄화 후, 셀룰로오스 탄화물의 섬유 구조를 저해시키는 문제점이 존재한다. 이러한 문제를 해결하기 위하여 탄소 나노튜브의 정제과정에서 연구된 액상, 기상 그리고 초음파 처리를 통한 정제방법들을 적용하여, 탄화 셀룰로오스에서는 초음파 처리를 통한 정제과정의 적용이 셀룰로오스 탄화물에서 섬유 구조가 증가하는 결과를 나타냈다.