The acid characteristics of natural montmorillonites produced in Pohang, Kyeongbuk, were modified by different alkali and/or acid treatments followed by ion exchanges with ammonium chloride solution. The removal of 1-octene from xylene mixture was carried out on those catalysts. The capacity of exchangeable hydrogen was 2 meq/100 mg clay on raw material, however, it increased up to 18 meq/100 mg clay by alkali and/or acid treatment and ion exchange. The modified montmorillonites showed much higher removal efficiency of 1-octene from xylene mixture than raw material. The removal efficiency was higher on alkali/acid-treated montmorillonites than on acid-treated ones. For the montmorillonites treated with only H2SO4, the removal efficiency increased with the concentration of H2SO4, reached maximum when treated by 15 wt% H2SO4. It was found that the removal efficiency was related with acidity and surface area of montmorillonites.

경북 포항지역에서 채취한 천연 몬모릴로나이트를 산과 알칼리로 처리하고 NH4Cl로 이온 교환시켜 산 특성을 변화시켰다. 그 시료들에 대하여 xylene 혼합물 중의 1-octene의 제거에 대해 연구하였다. 원광은 2 meq/100 mg clay의 치환성 수소량을 가지고 있었으며, 산ㆍ알카리 처리 및 이온교환을 통해 최대 18 meq/100 mg clay까지 치환성 수소량이 증가하였다. Xylene 혼합물로부터 1-octene의 제거 효율은 처리한 시료들이 원광보다 월등히 좋은 결과를 나타내었다. 황산과 염산 처리한 시료보다는 NaOH로 처리한 후 같은 조건으로 산처리한 시료가 우수하게 나타났다. 황산으로 처리한 시료에서 1-octene의 제거 효율은 황산의 농도가 증가함에 따라 증가하다가 15 wt%에서 최대 효율을 보였다. 올레핀의 제거 효율은 몬모릴로나이트의 산성도 및 비표면적과 관계있다는 것을 알 수 있었다.