Acrylic warp sizes were synthesized with very hydrophobic stearyl methacrylate (SMA) as the reactive cosurfactant in miniemulsion polymerization. Monomers with SMA were emulsified by high shear force of homogenizer and they were synthesized by semi-batch polymerization. The polymerization was confirmed by disappearance of C=C peaks in FTIR spectra of synthesized acrylic warp sizes. Increase of the SMA content in the synthesized acrylic warp sizes by increasing SMA content in the feed was confirmed by the increased -CH2peak intensity in FTIR spectra, due to long-chain alkyl group of SMA. The particle size and the stability of emulsion depending on the amount of surfactant used were examined by particle size analyzer and zeta-potential. We found the particle sizes were in the 64 ~ 186 nm range depending on the amount of surfactant used. The particle size became smaller and the zeta-potential values were increased with increasing the amount of surfactant used.

아크릴계 경사호제를 stearyl, methacrylate (SMA)를 반응성 공유화제로 사용하여 miniemulsion 중합법으로 제조하였다. 소수성 단량체를 유화시키기 위해 homogenizer를 사용하여 강한 전단력으로 균질화시켜 반연속식 중합법으로 합성하고 생성된 중합체의 FTIR 스펙트럼을 측정하여 SMA의 중합반응 및 합성된 중합체의 SMA함량에 대하여 확인하였다. 또한 입도분석기와 제타 전위 측정기로서 유화제 및 SMA의 함량에 따른 중합된 입자크기와 에멀젼의 안정성에 대해 연구하였다. 실험 결과, 합성된 공중합체의 FTIR 스펙트럼에서 남아있는 C=C 결합은 측정되지 않았으며 SMA의 함량이 증가할수록 SMA에 붙어있는 긴 알킬기 때문에 -CH2에 의한 흡수피크가 증가하였다. 유화제의 사용량에 따라서 호제의 입자크기는 64 ~ 186 nm의 분포를 나타내었으며, 유화제의 양이 증가할수록 입자크기는 작아졌고, 제타 전위값은 증가하여 균일하고 안정한 입자가 형성됨을 확인할 수 있었다.