In this work, the activated carbon fibers (ACFs) containing silver metal were prepared by Ag electroplating, in order to remove the toxic HCI. The surface properties of the ACFs were determined by using XRD and SEM measurements. 77 K/N2 adsorption isotherm characteristics, including the specific surface area and micropore volume, were investigated by BET and t-plot methods. Also, HCl removal efficiency was confirmed by a gas-detecting tube technique. As a result, Ag content on the ACFs increased with increasing the plating time. However, within the range of well-developed micropore structures, a slightly gradual decrease of adsorption properties, such as BET`s specific surface area and total pore volume, were observed by increasing the plating time. HCI removal efficiency of all Ag/ACFs except extremely treated sample (Ag-5) showed higher values than those of untreated ACFs. These results indicated that the presence of Ag on the ACFs played an important role in improving the HCI removal over carbon surfaces, due to catalytic reactions of ACFs-Ag-Cl.

본 연구에서는 독성가스의 한 종류인 염화수소(HCI)의 제거를 위해 활성탄소섬유(activated carbon fibers, ACFs)의 표면에 전해 은(Ag) 도금처리를 실시하였으며, 도입된 Ag가 활성탄소섬유의 표면과 기공특성 그리고 HCI의 제거에 미치는 영향을 살펴보았다. Ag가 도입된 활성탄소섬유의 표면특성은 XRD와 SEM을 통해 각각 관찰하였고, 77 K/N_(2) 등온 흡착특성은 BET식과 Boer의 t-polt을 이용하여 비표면적 미세기공의 부피를 확인하였다. 또한 HCI의 제거효율은 가스 검지관을 이용하여 측정하였다. 실험결과, 도금시간이 증가함에 따라 활성탄소섬유 표면의 Ag의 함량은 증가한 반면에 활성탄소섬유의 흡착특성인 비표면적과 미세기공부피 등은 점차 감소하였다. HCI의 제거효율은 미처리 활성탄소섬유에 비하여 Ag가 도입된 활성탄소섬유에서 높은 값을 보였지만. 일정량 Ag가 도입된 Ag-5의 경우는 감소하였다. 이를 통해 활성탄소섬유의 흡착특성과 표면에 도입된 Ag는 HCI의 제거에 있어서 중요한 역할을 하는 것으로 판단되어진다.