In order to improve the electrochemical properties of V_(2)O_(5) xerogel, Zn_(x)V_(2)O_(5) xerogels (x=0.01, 0.05, and 0.10) were synthesized by doping Zn into V_(2)O_(5) gel that was prepared via the reaction of V_(2)O_(5) powder with hydrogen peroxide, and their electrochemical properties as cathodes of secondary lithium batteries were investigated. The interlayer distance of Zn_(x)V_(2)O_(5) xerogels was in the ranges between 13.2 and 14.1 A. Linear sweep voltammograms revealed that as the Zn concentration in Zn_(x)V_(2)O_(5) xerogels increased, the reversibility improved. In the case of the Zn_(0.10)V_(2)O_(5) electrode, the specific capacity was more than 140 mAh/g at 10 mA/g discharge rate. The Zn_(0.10)V_(2)O_(5) electrode maintained 91% of the initial capacity after the 20th consecutive cycles.

리튬2차전지의 양극소재로 이용 가능한 V_(2)O_(5) 겔을 졸-겔법으로 합성한 후 미량의 아연을 도핑시켜 Zn_(x)V_(2)O_(5) xerogel (x=0.01, 0.05, 0.10)을 합성한 후 리튬2차전지 양극 소재로서의 전기화학적 특성을 연구하였다. Zn의 도핑된 양에 따라 층간 거리는 13.1~14.2 Å로 증가하였다. Zn의 도핑된 양이 증가할수록 가역적인 전기화학적 반응을 보였으며, Zn_(0.10)V_(2)O_(5) xerogel 전극에 10㎃/g의 방전전류를 인가하였을 때 140㎃h/g 이상의 비용량을 나타내었다. 셀에 50 ㎃/g의 인가전류로 20회 연속적으로 충ㆍ방전을 한 결과 Zn_(0.10)V_(2)O_(5) xerogel은 91%의 초기용량을 유지하였다.