Two kinds of maltose derivatives bearing cholesteryl group: maltose 6-cholesteryloxycarbonylpentanoates (CMTs) with degree of esterification (DE) ranging from 3.80 to 4 and acrylic esters of CMTs(CMTEs) were prepared. The networks with a liquid crystalline (LC) order were also prepared by photocrosslinking CMTEs in mesophase. The thermal and optical properties for both the uncrosslinked and crosslinked samples were investigated. All the uncrosslinked samples formed monotropic cholesteric phases with left-handed helicoidal structures and exhibited reflection colors over the full cholesteric range. This is the first report of a maltose derivative that formed thermotropic cholesteric mesophases with selective reflection bands in the visible wavelength region. The optical pitches (λ_(mS)) of all the uncrosslinked samples decreased with temperature or with DE at a given temperature. However. the λ_(m) of CMT was larger than that of at the same temperature and at the same DE. The networks did not display reflection colors, indicating that the cholesteric structure of CMTE were significantly changed upon crosslinking.

콜레스테릴 그룹을 지닌 두 종류의 말토오스 유도체, 즉 에스테르화도(degree of esterification, DE)가 3.80~4 범위에 있는 maltose 6-cholesteryl-oxycarbonylpentanoates (CMTs)와 CMTs의 아크릴산 에스테르들(CMTEs)을 제조하였다. 또한 액정 상태에 있는 CMTEs를 광가교시킴에 의해 액정 질서를 지닌 가교물질들을 제조하였다. 미가교와 가교된 시료들에 대한 열 및 광학 특성을 검토하였다. 모든 미가교 시료들은 좌측방향의 나선구조를 지닌 단방성 콜레스테릭 상을 형성하며 콜레스테릭 상을 형성하는 전 범위에서 반사색깔들을 나타냈다. 이것이 말토오스 유도체가 가시광 파장 영역에서 선택적인 반사대를 지닌 열방성 콜레스테릭 상들을 형성한다고 하는 최초의 보고이다. 모든 미가교시료들의 광학 피치들(λ_(m)′s)은 온도 상승 혹은 주어진 온도에서는 DE의 증가에 의해 감소하였다. 그러나 DE가 동일할 경우, 동일한 온도에서 나타내는 λ_(m)은 CMT가 CMTE에 비해 컸으며 가교 물질들은 반사색깔들을 나타내지 않았다. 이러한 사실은 CMTE의 콜레스테릭 구조가 가교에 의해 현저하게 변화되었음을 시사한다.