For the production of the double layered hollow microspheres with PS/PVA polymers using multiple emulsion (water/oil/water) method, various process conditions which can affect the particle size distribution of the final product have been studied. Experimeate results show that the average size tends to decrease with the increase of agitation time. RPM, and the reaction temperature of W_(l)/O emulsion. The particle size distribution however was not uniformly obtained for any . To obtain unifomi particle size distribution, ultrasonic treatment has been taken to the W_(l)/O emulsion. and by taking 30 seconds of ultrasonic treatment. double layered hollow microspheres of uniform size distribution around 0.35 μm have been produced.

Multiple emulsion (Water/Oil/Water)법을 이용하여 PS/PVA double layer를 갖는 고분자 중공 미세구를 제조하고자 하였으며, 이때 공정 변수들이 최종 생성물인 PS/PVA double layer 고분자중공 미세구의 크기와 입도분포에 미치는 영향을 조사하였다. 실험결과 PS/PVA double layer 고분자 중공 미세구는 1차반응인 W_(1)/O emulsion에서 교반속도, 교반시간, 반응온도가 증가함에 따라 입자들의 평균 size는 작아지는 경향을 나타내었으나 이들의 입도분포는 그다지 균일하지 못한 현상을 나타내었다. 입도의 균일성을 유지하기 위하여 W_(1)/O emulsion에서 초음파처리를 시도한 결과 초음파 처리 30 sec에서 입자크기 0.35 ㎛의 균일한 입도분포를 갖는 double layer 고분자 중공 미세구를 제조할 수 있었다.