In this study, the activated carbons (ACs) were prepared by ozone surface treatment to remove ammonia gas. The introduction of polar groups of (ACs) was confirmed by XPS analysis and the N2/77K adsorption isotherm characteristics of ACs, including specific surface area and micropore volume, were studied by Dubnin-Astakhov (D-A) equation. The ammonia removal efficiency was confirmed by gas-detecting tube technique. As a result, the specific surface area and micropore volume of ACs were slightly decreased as the ozone treatment time increased. However, the ozone treatment of ACs led to an increase in ammonia removal efficiency, mainly due to an increase of oxygen-containing functional groups of AC surfaces. This behavior was due to the improvementof adsorption capacity. which could be attributed to the acid-base interfacial interactions between ozonized ACs and ammonia.

본 연구에서는 암모니아 가스를 제거하기 위하여 활성탄소에 오존 표면처리 하였다. 오존 표면처리된 활성탄소 표면의 관능기 도입은 XPS 분석으로 조사하였고, 활성탄소의 비표면적과 미세기공 부피를 포함한 N₂/77 K 등온흡착특성은 Dubinin-Astakhov식 이용하여 확인하였다. 또한, 암모니아 제거성능은 암모니아가스 검지관을 이용하여 측정하였다. 본 실험결과, 오존의 표면처리 시간이 증가함에 따라 활성탄소의 비표면적 및 미세기공 부피의 파괴가 발생한 반면, 활성탄소의 암모니아 제거성능은 향상되었다. 이는 오존 표면처리된 활성탄소 표면과 암모니아 사이의 산-염기 계면 상호작용으로부터 활성탄소의 흡착용량이 증가한 것으로 판단된다.