Effects of the type and the composition of surfactant mixtures on morphology. average particle size and particle size distribution of a-alumina prepared by W/O emulsion method including combustion method were investigated. SP80 was used as a main surfactant, [SP80 & TW20] as well as [SP80 & TW80] as surfactant mixtures. As results, the above properties of alumina power prepared by using low mechanical agitation speed, 500 rpm. were not affected remarkably by the variation of type and composition of mixed-surfactants regardless of O : W volumetric ratio at fixed content of surfactant. However, under the conditions of 1 vol.% and 2 vol.% [SP80 & TW20] or [SP80 & TW80] of HLB_(m) = 5, O:W = 8 : 1 and 2000 rpm, the average particle size became much smaller and the range of particle size distribution was narrow in comparison with those obtained from the usage of single surfactant, SP80. These effects were enhanced when [SP80 & TW80] were used instead of [ST80 & TW20]. And also, under 4000 rpm, severe coalescence phenomena among alumina powder prepared by using 2.5 vol.% SP80 for O : W = 8 : 1.5 were reduced drastically by using 2.5 vol.%[SP80 & TW80] of HLB, -5.

리튬이 삽입된 흑연 층간화합물로부터 팽창흑연의 새로운 제조방법과 응용에 대하여 열처리 온도에 대한 팽창화 부피, 시트(sheet)상 흑연의 기계적 특성 및 원유의 흡유량 등을 연구하였다. 생성물의 팽창 부피는 Li 양과 열처리 온도의 증가와 함께 증가함을 보였다. 팽창흑연의 부피와 pH 농도 등의 두 가지 중요한 요소는 시트(sheet) 생성물의 품질과 기계적 특성에 영향을 주었다. 뿐만 아니라 여러 가지 Li 양과 제조 온도에 따른 팽창흑연에 원유의 흡착거동이 역시 연구되었다. 이들 연구 결과로부터, Li_(30)-EG850과 Li_(30)-EG900 팽창흑연의 최대 흡유량은 팽창흑연 1 g당 원유 69~81 g으로 상당히 높게 나타났다. 마지막으로, 시간에 의존하여 Li_(30)-EG의 최대 흡유량은 열처리 온도와 관련하여 흡유 시간의 증가와 함께 증가하였다.