This study investigated the dissolution property of nitrate salts in the desalination process with water and the stabilization property of residue after separating nitrates in a series of the processes for the radioactive sludge treatment. Desalination was carried out with the adding ratio of water and drying property was analyzed by TG/DTA, FTIR, and XRD. Nitrate salts involved in the sludge were separated over 97 wt% at the water adding ratio of 2.5. But a small quantity of calcium and sodium nitrates remained in the residue. These were decomposed over 500℃ and calcium carbonate, which was consisted mainly of residue, was decomposed into calcium oxide over 750℃. The residue have to be decomposed over 800℃ to reduce uranyl nitrate of six value into the stable U₃O^(8) of four value. As a result of removing the nitrates at the water adding ratio of 2.5 and drying the residue over 900℃, volume of the sludge waste decreased over 80%.

저실리카 X 제올라이트(LSX)의 합성에 대한 원료조성 및 온도에 의한 변화를 검토하였다. K₂O의 비율이 높은 혼합 Gel을 사용하면 보다 높은 온도범위에서도 순수한 LSX가 합성되었지만 결정화속도가 느려지고 입자의 크기가 커지는 경향이 있었다. K₂O의 비율이 낮아지면 합성시간이 짧아지고 결정입자의 크기는 작아지지만 LSX의 합성온도 영역이 감소하고 A형 제올라이트가 쉽게 생성되었다. 합성원료혼한 Gel을 저온에서 숙성하고 서서히 가열하는 방법으로 결정성이 높은 LSX를 24 h 이내의 비교적 짧은 시간에 합성할 수 있었다. LSX결정분말을 seed 물질로 원료 Gel에 소량 첨가한 결과 1㎛ 이하의 작은 LSX결정입자를 얻을 수 있었다. 합성 후에 버려지는 폐액의 약 72%를 합성원료로 반복해서 재사용하더라도 생성되는 LSX의 물성은 크게 달라지지 않았다.