Effect of the composition of mixing gel and temperature on the synthesis of low-silica X(LSX) zeolite was investigated. Although the pure LSX could be synthesized by using mixing gel with a higher K₂O ratio, the crystallization speed and particle size of LSX became slwer and larger, respectively. Decreasing the K₂O ratio had the effect which makes fast crystallization and makes crystal size small. However, the temperature range for LSX synthesis became narrow and formation of A-type zeolite was increased with decrease in K₂O ratio. Well crystallized LSX could by synthesized within 24h by aging at low temperature of 40℃ and slow heating. LSX crystalline particles with small size less than 1㎛ were obtained by addition of LSX crystals as seed material to the gel precursor. The waste solution after crystallization could be reused repeatedly without significant change in the properties of LSX synthesized.

규산나트륨과 플루오르화 규소산의 중화반응으로 제조된 실리카 슬러리를 이용하여 결정성 좋은 Na-magadiite를 합성하였다. 합성한 시료는 아민과 4급 암모늄염의 탄소 수를 달리하여 유기화하였다. 아민 처리한 magadiite의 d-spacing값은 아민의 농도가 증가할수록 증가하였으며, 탄소 수에 의존하여 14.1~35.7 Å의 d-spacing값을 나타내었다. 4급 암모늄염으로 이온 교환한 magadiite의 d-spacing값은 알킬기의 탄소 수에 의존하여 30.5~50.6 Å의 큰 증가를 보였다. 유기 처리된 magadiite의 열분석 결과는 아민 처리된 시료의 경우 100 ℃ 부근에서 급격한 무게 감량이 일어나는 반면, 4급 암모늄염 처리된 시료는 거의 200 ℃까지 무게 감량이 일어나지 않았다. 아민 혹은 4급 암모늄염 처리에 의한 magadiite의 유기화는 용이하게 진행되며, 층간 거리가 크게 확장되고, 열 안정성이 뛰어난 잘 분리된 엽상 구조의 유기화된 magadiite는 고분자 강화제로서 적절히 이용될 수 있을 것으로 기대된다.