Capability of loess ball on phosphorous removal in an artifical wastewater was investigated. Loess balls manufactured at various calcining temperature and size removed phosphate in the following decreasing order: 860℃ and Dia. 2-4 mm > 960℃ and Dia. 2-4 mm > 860 ℃ and Dia. 5-10 mm > 960℃ and Dia 5-10 mm. In a batch reactor, the removal of phosphate by Loess balls for temperature changes of the artificial wastewater showed that 30 > 25 > 20℃. The pH changes (pH 4, 5, 6, 7, 8, 9, 10) of the artificial wastewater (PO_(4)^(3-))-P 5 ppm) affected the removal of phosphate, 4 ppm with pH 4 and 2.5 ppm with pH 10 in 10 h. This also showed that the removal was more effective in acidic condition than in alkalic condition. Loess balls (860 ℃, Dia. 2-4 mm) in a continuous flow reactor with the artificial wastewater (PO_(4)^(3-))-P 5 ppm) removed phosphate of more 80%. Thus, loess balls for the removal phosphate of wastewater treatment should be chosen according to applications because a lower calcining temperature gives more effective removal of phosphate but has a lower strength.

본 연구는 황토볼을 사용하여 폐수 내에 존재하는 인의 제거능을 알아보고자 한다. 황토볼의 크기 및 소성온도의 변화에 따른 인 제거능은 황토볼(860℃, Dia. 2~4 mm) > 황토볼(960℃ Dia. 2~4 mm) > 황토볼(860℃, Dia. 5~10 mm) > 황토볼(960℃, Dia. 5~10 mm)의 순서를 보여주고 있다. 인공폐수의 수온 변화에 따른 인성분 제거능의 회분식 실험 결과는 30 > 25 > 20℃의 순서였으며, 인공폐수의 pH변화(pH 4, 5, 6, 7, 8, 9, 10)에 따른 회분식 실험 결과는 pH 4에서는 10 h 만에 4 ppm의 농도가 감소되었으나 pH 10의 경우에는 2.5 ppm의 농도가 감소되어 알칼리성에서 보다 산성에서 더 효율적임을 보여주고 있다. 연속흐름에 의한 인공폐수(5 ppm)의 인제거 실험결과는 황토볼(860℃, Dia. 2~4 mm)의 경우에 80% 이상의 인제거율을 보였다. 따라서 소성온도가 낮을 수록 인제거에 유리한 반면 황토볼의 강도는 약하게 되므로 여재로써 사용하기 위해서는 사용목적 및 방법에 따라 황토볼의 크기 및 소성온도를 결정해야한다.