In this study, experiments of uranium electrorefining in the molten salt were carried out in order to examine the effects of rotating the solid cathode and stirring the liquid camium cathode on the electrodeposition. Current density increases with an increase of rotation speed of the solid cathode. Although deposition rate increases in proportion to the rotation speed in the range of 14-20 rpm, it decreases in inverse proportion to the rotation speed above 20 rpm as a result of falling off the deposits. The size of deposits tends to reduce as the increase of current density, the deposits show spherical form and their size are almost uniform in the range of rotation speed more than 25 rpm. It was found that stirring the liquid cadmium cathode above 100 rpm avoids the formation of dendrite and results in the deposition of uranium.

본 연구에서는 용융염 내 우라늄의 전해정련에서 고체음극의 회전 및 액체음극의 교반이 석출에 미치는 영향을 알아보기 위한 실험이 수행되었다. 고체음극의 회전속도에 비례하여 전류밀도가 증가하였으며, 석출속도는 회전속도 14~20 rpm의 범위에서 회전속도에 비례하여 증가하였으나, 20 rpm 이상에서는 석출물의 물리적인 탈락으로 인해 반비례하여 감소하였다. 전류밀도의 증가에 따라 석출물의 크기는 줄어드는 경향을 나타냈으며, 약 25 rpm 이상의 회전속도에서는 구형의 석출물이 발생하여 석출물의 크기는 회전속도에 영향을 받지 않고 거의 균일하였다. 액체 카드뮴 음극을 100 rpm 이상으로 교반하면 생성된 dendrite를 파괴하여 액체 카드뮴 음극에 우라늄을 석출시킬 수 있음을 알았다.