The effects of shape, size, and contents of waste polyurethane foam on recycled foam was studied. The waste foam was treated in shape of powder, cube and bar type generated from rigid sandwich panel process. The tests for flexural strength, combustibility, and water absorptivity were carried out to investigate the mechanical and physical properties of the recycled foams. And the cell microstructure was evaluated through Scanning Electron Micrograph (SEM). The recycled foam containing powder-shaped underfilled and showed poor properties that was generated through reactivity of the resins and increasing of slurry viscosity. For the recycled foam with the cube and bar-shaped, the underfilling was caused by interference between the waste PUFs and increasing surface areas of PUF. Low cell density, non-uniformity of cell shape and size, and low adhesion of the boundary surface (new/recycled) was showed as a result of the poor properties. Considering underfilling and the properties ofPUF(new/recycled), maximum recycle contents were less than 20 wt% for the powder and above 40 wt% for the cube and bar.

실리카로부터 수열 조건에서 층상화합물의 일종인 마가다이트를 합성하고 합성된 마가다이트의 층간에 유기물의 층간 삽입을 통해서 유기 층상 마가다이트를 제조하였다. 생성물질들은 XRD, SEM, Solid NMR 등을 이용하여 분석하여 결정화 조건 및 층간 삽입조건에 대해서 조사하였다. 또한 나노 복합재용 층상화합물로 합성 마가다이트의 사용 가능성에 대해서 조사하기 위해서 여러 종류의 유기물을 층간에 삽입시켜 유기 층상 마가다이트를 제조 하였다. 건조된 유기 층상 마가다이트의 XRD 분석 결과로 001면의 basal-spacing값이 48~52Å으로 확장되었음을 확인할 수 있었고, 알킬 체인의 길이가 길수록 층간거리가 확장되었으나 C16이상에서는 알킬체인의 길이가 너무 길어 층간에 잘 들어 갈 수 없음이 확인되었다. 또한 APS를 층간삽입 시킨 시료는 solid-state ^(29)Si MAS NMR 분석 결과 실릴 결합이 성공적으로 일어났음을 확인할 수 있었다. 위에서 제조된 유기 층상마가다이트를 이용하여 에폭시 수지에 분산시켜 제조된 시료는 XRD와 TEM 분석 결과 분산과 박리현상이 잘 일어났음을 보여주고 있다. 이와 같은 결과로 볼 때 합성된 유기 층상 마가다이트는 우수한 나노복합재용 filler로 사용가능성을 제시하고 있다.