The effect of zeolite NaX on the reduction-carburization of WO_(3) with carbon monoxide was studied between 300-750 ℃. The zeolite NaX showed superior activity for the reduction-carburization of WO_(3) than that of silica gel white or sole WO_(3) under the same reaction conditions. The reactivity at 725 ℃ was best between 650∼750 ℃. The particle size was increased with reaction temperature. Particularly, the particle size, produced at 650 ℃, was determined to be nanophase size (50∼70 nm). However, the zeolite NaX was deactivated with carbon deposition by Boudouard`s reaction at temperature less than 700 ℃ but it was easily regenerated. This carbon deposition was not observed above 700 ℃. The results showed that the ultrafine tungsten carbide (<0.4 μm) was efficiently manufactured by the reduction-carburization of WO_(3) at 725 ℃ using zeolite NaX as a promoter.

CO를 이용하여 산화 텅스텐(WO₃)을 탄화 텅스텐(WC)으로 환원-탄화하는 공정에서 Zeolite NaX의 영향을 300~750℃의 온도구간에서 연구하였다. Zeolite NaX를 첨가할 경우 WO₃환원-탄화반응 효율이 동일한 가스 조성과 반응온도에서 WO₃단독 혹은 Silica gel white첨가에서 보다 우수함을 확인하였다. 650~750℃ 온도 구간에서의 Zeolite NaX를 이용한 탄화-환원반응은 725℃에서 반응성이 가장 우수하였다. 반응온도가 증가하면서 입자의 크기는 증가하는 것으로 확인되었고, 특히 650℃에서 제조된 탄화텅스텐의 입자크기는 50~70nm로 나노입자를 나타내었다. Zeolite NaX는 반응 중 carbon 침적에 의해 활성저하를 나타내는데 이는 쉽게 재생가능하고 700℃ 이상의 반응 온도에서는 carbon 침적이 발생하지 않았다. 이상의 결과로부터 Zeolite NaX를 효율 개선제로 첨가하여 725℃에서 WO₃를 환원-탄화하는 것이 초미립 탄화 텅스텐(WC)제조에 효과적인 것으로 판단된다.