Photocatalytic degradation of cyanide over UV/TiO_2 was studied with hydrogen peroxide as an oxidizing agent. Although oxygen is generally used as an oxidizing agent in the photocatalytic reaction, hydrogen peroxide was tested as an oxidizing agent to increase the degradation rate of cyanide. For UV/ TiO_2/ H_2O_2 system the degradation rate of cyanide gave a maximum in the neutral pH range. The addition of both oxygen and hydrogen peroxide as oxidizing agents did not show any synergistic effect on the degradation rate. Anatase-TiO_2 exhibited better activity than rutile-TiO_2 in the presence of oxygen, while in the presence of hydrogen peroxide, rutile-TiO_2 was better than anatase-TiO_2. The photocatalytic activity of UV/anatase-TiO_2/H_2O_2 decreased, however, due to the peroxo complex formed by the interaction of anatase-TiO_2 with hydrogen peroxide.

UV/TiO_2를 사용한 광촉매반응에 의해 시안이은(CN^-)을 광산화시키는 실험을 수행하였으며, 반응의 활성을 증대시키기 위하여 과산화수소를 도입하였다. 광촉매에 의한 반응에서 산화제로 산소를 사용하는 것이 일반적이지만, 본 연구에서는 산화제로 과산화수소를 사용하여 반응활성을 크게 증가시켰다 UV/ TiO_2/ H_2O_2 시스템에서 반응액이 중성일 때 반응활성이 가장 우수하게 나타났고, 산화제인 산소를 과산화수소와 동시에 사용하였을 때는 특별한 상승효과를 관찰할 수 없었다. 산화제로 산소를 사용하였을 때는 anatase 구조의 TiO_2가 활성이 우수하였고, 산화제로 과산화수소를 사용하였을 때는 rutile 구조의 TiO_2가 활성이 더 우수하였다. Anatase 구조의 TiO_2에 과산화수소를 산화제로 첨가한 경우에는 오히려 활성이 감소하였는데, 이는 과산화수소가 TiO_2와 반응하여 페르옥소 착화합물을 형성하였기 때문으로 해석하였다.