TiO_2 was synthesized by precipitation form aqueous TiOCl_2 solution, which was prepared by using HCI at various concentrations and reaction time. Pure rutile type TiO_2 was obtained when the concentrateon of HCI solution was 1.0M and 4.0M while a mixture of rutile and brookite was obtained at 2.0~3.5M HCL. There was optimem ration of Cl^-1_total/Ti^+4 in obtaining brookite-type TiO_2, and the ratio decreased with increased Ti^+4 concentration. The brookite transformed directly to rutile phase with increase of the reaction time only. The precipitation was delayed with increase of HCI concentration because the amount of H_2O which in necessary for the conversion of Ti^+4 to TiO_2, was relatively reduced. Therefore, in order to increase the productive efficiency it was required longer reaction time.

다양한 농도의 염산으로 제조한 Tioci2 수용액으로부터 반응시간에 따라 침전반응으로 TiO_2를 제조하였다. 1.0 M과 4.0 M 염산을 사용하여 얻은 분말의 결정구조는 순수한 루틸상이고, 2.0 M~3.5 M에서는 브루카이트상과 루틸상의 혼합상이 생성되었다. 브루카이트상이 지배적인 결정구조를 이루는 TiO_2 제조를 위한 용액의 적정 Cl^-1_total: Ti^+4의 비율이 존재하며, TiOL_2 수용액의 Ti^+4 농도가 증가할수록 브루카이트상이 생성되기 위한 Cl^-1_total: Ti^+4의 비율이 감소였다. 브루카이트상 TiO_2는 반응시간의 증가에 따라 루틴상으로 직접 상변화가 진행되었다. 또한, 염산농도가 증가할수록 Ti+4이 TiO_2로 전환되는데 필요한 산소의 공급원인 H_2O의 양이 상대적으로 작아서 침전반응이 느리게 진행되었으며, 생성효율의 증가를 위해서는 반응시간의 증가가 필요하였다.