Thermal behaviours of V_2O_5/TiO_2 catalysts with different V_2O_5 contents (1.0, 3.0, 5.0, and 10.0 wt%) were investigated in a microreactor using BET surface measurement and XRD. The activities of catalysts before and after a thermal treatment were tested in the Selective Catalytic Reduction (SCR) reaction. Both structural and catalytic investigations showed an evidence that the sintered anatase affected both the surface of species and the growth of ammonium vanadate on calcinations. The catalytic tests exhibited that the activity of catalyst containing 1.0, 3.0, and 5.0wt% V_2O_5 increased on calcination. However, the activity of catalyst containing 10.0 wt% V_2O_5 decreased due to the extensive loss of surface area on calcination. The catalyst containing 5.0 wt% V_2O_5 had high catalytic activity and good thermal stability.

V_2O_5의 함량(1.0, 3.0, 5.0, 10.0 wt%)에 따른 V_2O_5/TiO_2 촉매의 열적 거동을 Microeactor와 BET 표면적 측정 그리고 XRD를 이용하며 조사하였다. 열처리를 통하여 제조한 촉매의 활성은 선택적 촉매환원 반응을 통하여 측정하였다. V_2O_5의 함량과 반응온도, Space Velocity 및 MH_3 공급량에 따른 V_2O_5/TiO_2 촉매의 활성반응 평가를 통해 각각의 영향을 분석하였다. 또한, 같은 조건에서 BET, XRD을 이용하여 비표면적과 구조변화를 조사하였으며 반응에서의 역할을 분석하였다. 촉매의 함량에 따른 선택적 촉매환원 활성을 측정한 결과 1.0과 3.0 그리고 5.0 wt%에서는 증가하는 경향을 보인 반면에 10.0 wt%에서는 감소하는 경향을 보였다. V_2O_5 함량이 10.0 wt%일 때의 촉매 비표면적이 넓은 감소 곡선 경향을 나타냈으며, V_2O_5 함량이 5.0 wt%일때 가장 높은 활성과 우수한 열안정성 결과들 사이에서 최적의 조건을 확인할 수 있었다.