Zeolite X/activated carbon composite (zeocarbon) was synthesized from rice hulls. The adsorption equilibrium of H_2O on zeocarbon was compared with that of zeolite 13X, Langmuir-Freundlich, Excess Surface Work (ESW) and Multi-BET isotherm models were used to fit the experimental data of H_2O adsorption on zeocarbon and zeolite 13X. In the case of zeocarbon, the minimum error of 1.39% resulted when the Langmuir-Freundlich model was applied at 313.15 K. In the cases of Multi-BET and ESW models, the minimum errors were 2.29% and 0.47% at 131.15 K and 353.15 K, respectively. In the case of zeolite 13X, the minimum error was 0.10% at 0.68%, at 313.15 K and 353.15 K, respectively. ESW model was found to be in better agreement with the experimental values than Langmuir-Freundlich model or Multi-BET model. Considering that monolayer adsorption occurs in low-pressure region, while the capillary condensation phenomenon prevails in high-pressure region, ESW model fitted well under all the temperature and pressure conditions.

왕겨를 출발 원료로 하여 제올라이트 X/활성탄 복합체(제오카본)를 합성하였으며, 합성된 복합체와 제올라이트 13X애 대한 H_2O의 흡착 특성을 비교 하였다. 실천을 통해 얻어진 흡착 등온선에 Langmuir-Freundlict, Muilt-BET 및 Excess suface Work (ESW) 모델을 적용 시켰다. 결과에서 알수 있듯이, 제오카본의 경우에는 Langmuir-Freundlich 모델을 적용했을 경우에는 313.15 K (1.39%), Multi-BET 모델의 경우에는 313.15 K (2.29%), ESW 모델 적응시는 353.15 K (0.47%) 온도에서 가장 작은 오차를 보여주었다. 제올라이트 13X외 경우에는 Langmuir-Freundlich 모델을 적용했을 경우에는 353.15 K (0.10%), Multi-BET 모델의 경우에는 313.15 K (0.65%), ESW 모델 적용시는 353.15 K (0.68%) 온도에서 가장 작은 오차를 보여주었다. 특히, ESW 모델은 Langmuir-Freuntdlich Mulit-BET model에 비해서 저압영역에서는 단분자충 흡착과 고압 영역에서는 capillary condensation 현상 등이 고려된 결과, 모든 온도와 압력 범위에서 잘 적용되었다.