In this work the effect of composition in a diglycidylether of bisphenol A (DGEBA) and polyimide (PMR-15) blend system on the cure behaviors and thermal stabilities were investigated. The cure behaviors were studied in Near-IR and DSC measurements, and thermal stabilities were also carried out by DMA and TGA analyses. DDM (4,4`-diamino diphenyl methane) was used as a ruling agent for DGEBA and the content of PMR-15 in the mixture was 0, 5, 10, 15, and 20 phr. As a result the conversion ( a ) was slightly decreased as the content of PMH-15 was increased. The maximum owe activation energy (E_a) occurred at (IDT) phr of PMR-15. From the TGA results of DGEBA/PMR-15 blend system the thermal stabilities based ort the initial decomposition temperature (IDT) and integral procedural decomposition temperature (IPDT) rose with increasing the PMR-15 composition. The critical stress intensity factor (K_IC) showed a similar behavior with E_a , possibly due to the cross-linking developed by the interactions between inter-molecules of the polymer chains.

본 연구에서는 DGEBA/PMR-15 블렌드계에서 조성비가 경화거동 및 열안정성에 미치는 영향에 대하여 고찰하였다. 경화거동은 Near-lR과 DSC를 이용하였고, 열안정성은 DMA와 TGA를 통하여 고찰하였다. DGEBA에 대한 경화제로는 DDM출 사용하였으며, PMR-15의 조성비는 0, 5, 10, 15, 그리고 20 phr로 하였다. 본 실험 결과, PMR-15의 함량비가 증가함에 따라 전화율이 약간씩 감소하는 경향을 보였으며, 경화 활성화 에너지(E_a)는 함량비에 따라 점차 증가하다가 10 phr에서 최고값을 나타내었다. 그리고 DGEBA/PMR-15 시스템의 TGA 분석 결과 열분해 개시온도(initial decomposition temperature, IDT)와 적분 열분해 진행 온도(integral procedural decomposition temperature, IPDT) 등에 입각한 열안정성은 PMR-15의 함량이 증가할수록 증가하였다. 기계적 특성인 K_IC는 E_a와 유사한 경향을 나타내었는데 이는 PMR-15의 조성의 변화가 분자들간의 상호작용으로 인한 가교구조 형성에 영향을 미쳤기 때문인 것으로 사료된다.