The chelating polypropylene adsorbents were prepared by radiation-induced grafting technique using 2,3-epoxypropylmethacrylate (GMA) as the monomer, followed by amination with five different amines. It was found that the degree of grafting increased with reaction temperature and absorbed radiation dose. Every amination reaction occurred rapidly to reach the maximum content of amine. The extent of amination, under the same reaction condition, was in the increasing order: EDA>DETA>HMDA>DMA>DEA. Adsorption capacities of the prepared adsorbents for lead ion increased with adsorption temperature, amine content and pH of the ionic solution. For practical applications, selective adsorption characteristics for lead ion were investigated using diethylenetriamine (DETA), which had the highest adsorption capacity among the modified adsorbents that were prepared. It was found that the adsorption capacity of adsorbents prepared in this study was higher than commercial adsorbents.

전조사법에 의해 폴리프로필렌 부직포 상에 2,3-에폭시프로필메타크릴레이트(GMA)를 그라프트 공중합시킨 후, 아민화 반응을 통하여 5종류의 아민그룹을 도입함으로써 킬레이트화 중금속 흡착제를 제조하였다. 그라프트 반응시의 그라프트율은 반응온도와 조사시의 흡수선량이 증가함에 따라 함께 증가하였다. 아민화 반응속도는 전체적으로 매우 빨랐으며, 동일조건에서의 반응성은 EDA>DETA>HMDA>DMA>DEA의 순서를 따랐다. 다양한 아민그룹이 도입된 흡착제의 납 이온 흡착효율을 비교한 결과 디에틸렌트리아민(DETA)이 도입된 흡착제가 동일조건에서 가장 높은 흡착성능을 나타내었는데, 흡착온도와 아민함량, 이온용액의 pH값이 증가함에 따라 흡착효율도 함께 증가하였다. 실제적인 응용을 위하여 DETA가 도입된 흡착제를 사용, 납 이온에 대한 선택적 흡착성능을 고찰한 결과 다른 이온이 높은 농도로 공존하는상태에서도 우수한 흡착성능을 가지는 것으로 평가되었다.