Using polypyrrole, instead of common MnO2, a tantalum condenser was polymerized to study its characteristics as a solid electrolyte. Considering production cost and efficiency, a chemical oxidation method was used for the polypyrrole polymerization. Concentration of an oxidizing agent, number of repeated polymerization, and combination and order of oxidizing agents used were selected as the main parameters for this study. Tantalum condensers were produced by several polymerization processes: one-step, multi-step, complex-step and reverse complex-step. With the complex-step polymerization process, the best condenser characteristics were obtained. It was found that the degree of pore filling of the sintered tantalum pellet with polypyrrole depended strongly on the oxidizing agent's concentration, less on the number of repeated polymerization, and the least on the combination and order of the oxidizing agents used.

기존의 MnO2 대신 폴리피롤을 전해질로 적용한 탄탈륨 고체전해질 콘덴서를 제작하여 그 특성을 고찰하였다. 폴리피롤의 적용은 생산원가 및 효율성을 고려하여 화학적인 산화중합 방법을 채택하였으며, 산화제의 농도, 중합회수, 중합방법을 주요변수로 선정하였다. 콘덴서는 폴리피롤 중합단계를 단단계공정, 다단계공정, 복합공정 및 역복합공정으로 구분하여 제작하였으며, 복합공정으로 2회 폴리피롤 중합하는 방법이 가장 우수한 콘덴서 특성을 기록하였다. 산화제의 농도에 따라 폴리피롤의 소자 pore에 대한 막힘 정도가 매우 중요하며, 이는 산화제의 농도, 중합반응회수 및 산화제 농도의 적용 순서 등에 의존하는 것으로 확인되었다.