Recycling of PP/EPR based bumper coated with polyester urethane paint has been performed by a chemical decoating method. Physical properties and processability of recycled materials have been investigated by dynamic mechanical thermal analysis, impact test and melt flow index measurement. Morphological change of EPR, degree of distribution and dispersion during the recycling process seem to be the most important factor for the optimal mechanical properties of recycles materials. When the ratio of recycled/virgin resin was higher than 0.5, significant decrease in the mechanical properties was observed. It is suggested that concentration of the recycled PP/EPR resins in compounding must be lower than 40 weight percent to have acceptable mechanical properties.

폴리에스테르 우레탄 도료로 코팅된 범퍼를 화학적 박리방법을 이용하여 도막을 제거한 후 수지를 재생하였다. 재생 수지 함량에 따른 범퍼의 물리적 성질 및 가공성을 조사하기 위하여 동적 기계적 열분석, 충격 시험 및 용융흐름지수(MFI)를 측정하였으며, 모폴로지 변화를 조사하기 위하여 주사전자현미경을 사용하였다. 그 결과, 버진 수지에 재생 수지의 함량을 증가시킴에 따라 물성이 저하됨을 확인할 수 있었는데, 이는 범퍼 수지의 여러 재생 공정 중에 발생할 수 있는 EPR(Ethylene Propylene Rubber) 탄성체의 모폴로지 변화와 PP/PE 블록 공중합체와 EPR 탄성체의 분산 및 분포 변화가 가장 큰 원인임을 주사전자현미경 결과를 통해 알 수 있었다. 따라서, 범퍼수지의 종합물성 재현을 위해서는 버진 수지에 재생수지를 40 wt% 이하로 첨가하는 것이 바람직하다는 것을 알 수 있었다.