EPDM used as an electrical insulating material was blended with silicone rubber and compatibilizer to improve weatherability, ozone resistance, and dielectric strength. The compatibilizer was prepared by imidizing maleated EPDM with α, ω-aminopropyl polydimethylsiloxane. EPDM/silicone alloy was prepared by blending EPDM and silicone rubber with weight ratio of 9/1, 7/3, 5/5, 3/7 and 1/9, maleated EPDM-polydimethylsiloxane copolymer, and dicumyl peroxide (DCP). The maximum tensile strength of 0.177 kgf/mm(2), elongation at break of 257%, and dielectric breakdown voltage 362.25 kV/cm were obtained from the alloy prepared with 9 to 1 weight ratio of EPDM/silicone. The compatibility of the alloy was confirmed from the thermal characteristics measured using DMA and DSC. The morphology of the alloys was observed with SEM.

전기절연재료로 사용되고 있는 EPDM을 내후성, 내오존성 및 유전강도를 향상시키기 위하여 실리콘 고무와 알로이를 제조하였다. 상용화제는 EPDM에 maleic anhydride (MA)를 그라프트시켜 말레화 (EPDM-g-MA)을 제조한 다음, α,ω-aminopropyl polydimethylsiloxane을 이미드화 반응으로 도입하여 제조하였다. EPDM/실리콘 알로이는 EPDM과 실리콘 고무 배합비를 중량비로 9/1, 7/3, 5/5, 3/7, 및 1/9로 하고, 말레화 EPDM-polydimethylsiloxane 공중합체를 상용화제로, 그리고 dicumyl peroxide (DCP)를 가교제로 사용하여 제조하였다. 가교된 알로이의 기계적 강도를 측정한 결과 EPDM/실리콘의 배합비가 9/1인 경우 최대 인장강도가 0.177 kgf/min(2), 신장율이 257.4%로 가장 높은 값을 나타내었으며, 절연파괴전압은 362.25 kV/cm로 가장 우수하였다. 알로이의 열적특성을 DMA 및 DSC로 관찰하여 상용성을 확인하였으며, 제조한 알로이의 모폴로지는 SEM으로 관찰하였다.