The preparation of polymeric dental restorative materials was carried out using a 3-component multiple hybrid filler system. This system was composed of radio-opaque barium silicate microfiller, fused silica macrofiller, and fumed silica submicrofiller, and the surface was treated with γ-methacryloxypropyltrimethoxysilane to improve the miscibility with bisphenol. A glycerolate dimethacrylate and triethylene glycol dimethacrylate resin matrix. Also, effects of photoinitiator (camphorquinone) and photoaccelerator [ethyl-4-(N, N'-dimethylamino)benzoate] on the degree of conversion of dental materials were investigated by using FT-IR spectroscopy. In addition, diametral tensile strength, polymerization shrinkage, and water absorption of dental materials were measured. Optimization of dental properties was also investigated by comparing with those of available commercial products.

실리카계 submicrofiller, 방사선 불투과성의 바륨 실리케이트 microfiller 및 fused 실리카 macrofiller를 균일하게 혼합한 삼성분계 multiple hybrid filler system을 사용하여 가시광선 중합형의 고분자계 치과용 복합레진을 제조하였다. Bisphenol A glycerolate dimethacrylate와 이의 점도 희석제인 triethylene glycol dimethacrylate를 적정량 배합하여 resin matrix로 사용하였으며 이들 resin matrix와 충진재와의 혼화성을 증가시키기 위해 소수성의 충진재표면을 γ-methacryloxypropyltrimethoxysilane을 사용하여 소수성으로 개질시켰다. 적정량의 광개시제 camphorquinone과 광환원제인 ethyl-4-(N,N'-dimethylamino)benzoate를 사용하여 제조한 고분자계 치아 수복재에 대하여 FT-IR을 사용하여 중합전환률을 측정하였다. 또한 제조된 복합레진의 diametral tensile strength, 중합수축률 및 물흡수도 등을 측정하여 선진 제품과 비교, 분석함으로써 제조된 복합레진의 치과적 물성의 최적화에 대하여 고찰하였다.