The objective of this study is to investigate the removed T-P and turbidity in wastewater treatment process using Autoclaved Lightweight Concrete (ALC). ALC was used as a packing material and supporters. Effects of several physical factors on the phosphorous, turbidity and BOD removal efficiencies were examined by using artificial waste water(T-P: 115∼170 ppm, turbidity: 950 NTU, TDS: 150∼700 ppm and BOD: 200 ppm). Morphology of ALC was investigated by the SEM. The specific area which measured by BET was 27.66 ㎡/g. The results showed that the ALC was effective material as an adsorbent due to its structure and porosity. It was found that turbidity removed was 95∼98%; phosphate removed was 85∼90%; and BOD removed was 90%. Agitation process was more effective than aeration process in the removal of phosphate and BOD.

본 연구는 경량기포콘크리트를 폐수처리공정에 활용하기 위한 목적으로 진행되었다. 경량기포콘크리트를 흡착제로 사용한 경우와 교반형태와 폭기형태의 반응기에서 사용하였을 경우의 탁도원인물질 및 총인 성분의 제거 효율 및 BOD 제거에 대한 실험을 실시하였다. 본 연구에서는 탁도는 950NTU, 총용존고형물은 약 700 ppm, 그리고 총인의 농도는 115∼170ppm이며, BOD는 200ppm인 인공폐수를 대상으로 실시하였다. SEM과 BET 방법에 의하여 ALC의 구조 및 비표면적을 분석한 결과 비표면적은 27.66 ㎡/g 이었다. 본 실험조건에서 총인의 85% 정도가 제거되고 탁도는 99% 정도가 제거되며 BOD는 90% 정도가 제거되었다. 경량기포콘크리트를 폐수처리공정에 사용할 경우 반응의 형태에 따라서는 탁도원인물질은 폭기공정에서 처리효율이 우수하며, 총인성분 및 BOD의 제거는 교반공정에서 제거효율이 우수하였다.