Activated carbon filter (A/C filter) for the air purification was prepared using powdered activated carbon, polyurethane foam (PUF) sheet, binder and dispersion agent. Binder and dispersion agent used were vinyl acetate ethylene (VAE) and carboxy methyl cellulose (CMC), respectively. Impregnation, roll pressing and drying was all done in a continuous process to prepare A/C filter. The effectiveness of A/C filter was determined by types of powdered activated carbon, binder and dispersion agent. Their optimum ratios were found to be 1:6:6, respectively. Dispersion agent was effective preventing a decline in the adsorption capacity of A/C filter, and the effect was thought to be caused by removal of water film phenomenon.

다공성 polyurethane foam (PUF)에 수용성 접착제를 사용하여 분말 활성탄을 부착한 공기 활성탄 필터를 제조하였다. 접착제는 vinyl acetate ethylene (VAE), 분산제로는 carboxy methyl cellulose (CMC)를 사용하였으며, 제조방법은 분말 활성탄, 접착제 그리고 분산제의 혼합액에 PUF를 연속 통과시킨 후 압착, 건조과정을 거치는 연속공정이었다. 공기 정화용 필터로서의 제반 성능은 접착제와 분산제의 종류 및 혼합액 제조시 활성탄, 접착제 그리고 분산제의 배합비에 영향을 받았으며, 이들 성분의 최적 재합비는 중량기준으로 1:6:6이었다. 특히 분산제는 수용성 접착제 사용에 의한 수막 현상 제거도 공기 정화용 필터 흡착능 저하 방지에 좋은 결과를 보았다.