The preparation of antibacterial polymeric dental restorative composites was carried out using silver/zirconium-phosphoric acid(AZPA) inorganic antibacterial agent and chitosan. In order to improve the mechanical properties of dental composites, initially, the surface of fumed silica microfiller was treated with γ-methacryloxypropyltrimethoxysilane. Diametral tensile strength, flexural strength, Knoop hardness, antibacterial, and antifungal properties of dental composites were investigated. The optimum concentration of AZPA was 2∼4 wt% of silica filler used based on 60 wt% of loading onto 2.2'-bis-[4-(3-methacryloxy-2-hydroxypropoxy)phenyl]propane/triethyleneglycoldimethacrylate (70/30 wt%) resin matrix. Addition of chitosan to AZPA enhanced the antibacterial properties of restorative materials

은-지르코늄인산계(AZPA) 무기항균제와 키토산이 단독 혹은 혼합 첨가된 고분자계 치아수목재를 제조하였다. Resin matrix 내 충진재의 분산성 향상과 치아수복재의 기계적 특성을 향상시키기 위해 실리카 충진재 표면을 γ-methacryloxypropyltrimethoxysilane을 이용하여 소수성으로 처리하여 사용하였다. 제조된 치아수복재의 대표적 기계적 물성인 간접인장강도, 굴곡강도, Knoop 경도값 및 항균 특성에 대한 항균제의 효과를 고찰하였다. 그결과, 사용된 resin matrix 인 2,2'-bis-[4-(3-methacryloxy-2-hydroxypropoxy)phenyl]propane/triethyleneglycoldimethacrylate (70/30 wt%)에 대한 충진재의 충진률이 60 wt%일 때 AZPA의 함량이 충진재를 기준으로 2∼4 wt%일 때가 최적의 물성을 보임을 알 수 있었다. 또한 키토산을 혼합 사용한 경우 수복재의 기계적 물성의 큰 변화없이 항균특성이 매우 향상됨을 알 수 있었다.