This review article summarizes three method to assemble zeolite monolayers on glass via covalent linkages. The first method involves covalent linkage between the 3-aminopropyl and 3-(2,3-epoxypropoxy) propyl groups tethered to the external surfaces of zeolite crystals and glass, respectively. The zeolite crystals tended to pack with one-dimensional orientation. The second method takes advantage of facile N-H addition of amino groups onto the double bonds of fullerene. Thus, fullerene was employed as the linker to connect the 3-aminopropy1 groups tethered to both zeolite crystals and glass. A careful investigation of the intermediate steps of the monolayer assembly revealed that the close packing of zeolite crystals occur via surface migration of the crystals initially soft-landed on the surface randomly. The third method involves the direct connection between the glass-bound 3-halopropyl groups with the hydroxyl groups on the surface of zeolite crystals. This method is simple hence economical. This review also introduces a method to micropattern zeolite monolayers on glass by modifying the microcontact printing method.

이 총설은 제올라이트 결정들을 기본 빌딩블록으로 간주하여 유리판 위에 공유결합을 통하여 제올라이트 단층 막을 형성하는 세 가지 방법을 소개하고 있다. 첫 번째 방법은 제올라이트 결정 및 유리 표면에 존재하는 히드록실기(-OH)와 알콕시실릴(Si-OR) 또는 할로실릴(Si-X) 화합물 간의 반응성을 이용하여 이들 표면에 각각 3-아미노기와 에폭시기를 매단 후 친핵성고리열림반응을 통하여 이들 기능기를 공유결합으로 연결하여 결국 제올라이트 결정들을 단층으로 유리 표면에 정렬시키는 방법이다. 제올라이트 결정들은 넓은 면이 유리판과 평행하게 그리고 밀집하여 정렬하는 경향을 보인다. 두 번째 방법은 우선 유리판과 제올라이트 결정 표면에 아미노기를 부착시킨후 풀러렌(C60)을 연결자로 이용하여 이들을 공유결합으로 엮어서 결국 유리판위에 제올라이트 단층막을 형성하는 방법이다. 이 반응의 중간과정을 세밀히 살펴본 결과 제올라이트 결정들이 우선 무질서하게 유리판 위에 약하게 결합한 뒤에 표면을 따라 재이동하여 서로 밀집한다는 사실을 알게 되었다. 세 번째 방법은 유리판에만 할로프로필기를 부착시킨후 아무 처리도 하지 않은 제올라이트와 반응시켜 유리판 위에 제올라이트 단층막을 형성하는 경제적인 방법이다. 이 방법을 이용하면 실리카 또는 알루미니와 같은 거친 표면에 제올라이트 단층막을 형성하기가 용이하다. 또한 세 번째 방법을 응용하여 위에 제올라이트 단층막을 미세패턴의 형태로 도포하는 방법도 소개된다.