A series of new wholly aromatic polyesters having alkoxy group in the side chains were synthesized by the solution polycondensation from 2,5-dialkoxyterephthaloyl chlorides with 1,4-bis(p-hydroxybenxolyloxy)benzene. The resulting polyesters have been characterized by H-NMR, FT-IR, DSC, TGA, optical polarizing microscope and x-ray diffractometer. The inherent viscosities (ηinh) measured at 35℃ in phenol/p-chlorophenol/1,1,2,2-tetrachloroethane(24/40/35 w/w/w) were 0.56~0.98 dL/g. The glass transition temperature (Tg) and the melting temperature(Tm) decreased with increasing the length of the alkoxy side chain. The initial decomposition temperatures as measured by TGA occurred at 338~369℃ in N2gas and thermal stability decreased with increasing the length of the side chains. Above the melting temperature, the polymers showed the schieren textures which are indicative a nematic phase. WAXS-diffractograms showed that the polymers with side chains were crystalline at room temperature. Especially, analysis of a few sharp reflections in the small-angle region, suggests that these polymers crystallize to layered structures.

곁사슬에 알콕시 그룹을 갖는 일련의 새로운 전방향족 폴리에스테르를 1,4-bis(p-hydroxybenxolyloxy)benzene과 2,5-dialkoxyterephthaloyl chloride를 사용하여 용액중합법에 의하여 합성하였다. 이들 중합체들은 H-NMR, FT-IR, DSC, TGA, 편광현미경 및 X-ray 분석기 등을 사용하여 여러 가지 특성조사를 행하였다. 중합체들의 고유점도(ηinh)는 0.56gL/g이었고, 유리전이온도(Tg), 용융온도(Tm) 및 초기 열분해온도(Tdi)의 경우 곁사슬의 길이가 증가함에 따라 감소하는 경향을 보였다. 곁사슬을 갖는 모든 중합체들은 용융온도 이상에서 네마틱 액정상임을 나타내는 schlieren 무늬가 관찰되었다. X-선 분석결과 n=1 인 중합체를 제외한 모든 중합체들은 낮은 각도 영역에서 예리한 회절곡선이 관찰되었고, 이들이 층상구조 형태로 결정화 되었음을 확인하였다.